Improving the Properties of Biodegradable PLA via Blending with Polyesters for Industrial Applications

Zehra Kuru1✉,
Mehmet Arif Kaya2
1Tisan Mühendislik Plastikleri, R&D Center
2Yalova University
Published:December 31, 2022
DOI: 10.56038/ejrnd.v2i4.201
Vol. 2, No. 4

Abstract

Polylactic acid (PLA) is a biodegradable polymer obtained from the fermentation of renewable resources, which can also be used in industrial areas. The employment of PLA is restricted by its brittle nature at room temperature. This study, it is aimed to prepare PLA blends with PBT (Polybutylene terephthalate) to overcome this drawback. Thus, it can be provided new raw materials to many sectors, especially textile, automotive and electronic products, by preparing biodegradable, environmentally friendly materials with better performance properties. PLA/PBT blends containing 5%, 10%, and 15% PBT by weight were produced in a twin screw extruder using with using maleic anhydride grafted ethylene/butyl acrylate (EBA-g-MAH) as a compatibilizer. For comparison studies, blends of PLA/PBT without compatibilizer were also prepared. Examinations on the flow, viscoelastic properties, and rheologic characteristics of prepared samples were carried out by using Melt Flow Index values and Rotational Rheometer measurements. Mechanical and impact resistance characteristics were identified in accordance with the relevant standards. Physical properties of blends such as molding shrinkage, density, and hardness values were also determined. Degradation or cross-linking-induced changes in the chain structure was not observed during the investigation via using a rotational rheometer for PBT samples at 240 °C /15 min., and PLA samples at 260 °C /15 min. Notched izod impact test results show that adding compatibilizer increases 16% impact resistance of PLA/PBT blends. The tensile modulus values of the blends containing compatibilizer decreased by 2% approximately. These results show the transition from brittle to ductile behavior of PLA for compatibilized blends.

Keywords
Polylactic acidPolybutylene terephthalatePLA blendsCompatibilization

References

  1. 1.R. Auras, B. Harte, and S. Selke, Macromol. Biosci., 4, 835 (2004).
  2. 2.R.E. Drumright, P.R. Gruber, and D.E. Henton, Adv. Mater., 12, 1841 (2000).
  3. 3.R. Auras, B. Harte, S. Selke, An overview of polylactides as packaging materials, Macromol. Biosci. 4 (2004) 835–864
  4. 4.R. Datta, M. Henry, Lactic acid: recent advances in products, processes and Technologies a review, J. Chem. Technol. Biotechnol. 81 (2006) 1119–1129.
  5. 5.J. Lunt, Large-scale production, properties and commercial applications of polylactic acid polymers, Polym. Degrad. Stab. 59 (1998) 145–152.
  6. 6.J.C. Middleton, A.J. Tipton, Synthetic biodegradable polymers as orthopedic devices, Biomaterials 21 (2000) 2335–2346.
  7. 7.K.E. Perepelkin, Polylactide fibres: fabrication, properties, use, prospects. A review, Fibre Chem. 34 (2002) 85–100.
  8. 8.Scheirs J., Long T. E.: Modern polyesters: Chemistry and technology of polyesters and copolyesters. Wiley, Chichester (2003).
  9. 9.Peters E. N.: Engineering thermoplastics – Materials, properties, trends. in ‘Applied plastics engineering handbook’(ed.: Kutz M.) William Andrew Publishing, Oxford, 3–26 (2016).
  10. 10.https://doi.org/10.1016/B978-0-323-39040-8.00001-8DOI
  11. 11.Genovese L., Lotti N., Gazzano M., Siracusa V., Dalla Rosa M., Munari A.: Novel biodegradable aliphatic copolyesters based on poly(butylene succinate) containing- thioether-linkages for sustainable food packaging applications. Polymer Degradation and Stability, 132, 191–201 (2016).
  12. 12.https://doi.org/10.1016/J.polymdegradstab.2016.02.022DOI
  13. 13.Auras R., Harte B., Selke S.: An overview of polylactides as packaging materials. Macromolecular Bioscience, 4, 835–864 (2004).
  14. 14.https://doi.org/10.1002/mabi.200400043DOI
  15. 15.Muller R-J., Kleeberg I., Deckwer W-D.: Biodegradation of polyesters containing aromatic constituents. Journal of Biotechnology, 86, 87–95 (2001).
  16. 16.https://doi.org/10.1016/S0168-1656(00)00407-7DOI
  17. 17.Di Lorenzo M. L., Rubino P., Cocca M.: Isothermal and non-isothermal crystallization of poly(L-lactic acid)/ poly(butylene terephthalate) blends. Journal of Applied Polymer Science, 131, 40372/1–40372/8 (2014).
  18. 18.https://doi.org/10.1002/app.40372DOI
  19. 19.Santos L. G., Costa L. C., Pessan L. A.: Development of biodegradable PLA/PBT nanoblends. Journal of Applied Polymer Science, 135, 45951/1–45951/9 (2018).
  20. 20.https://doi.org/10.1002/app.45951DOI
  21. 21.Di Lorenzo M. L., Rubino P., Cocca M.: Miscibility and properties of poly(L-lactic acid)/poly(butylene terephthalate) blends. European Polymer Journal, 49, 3309–
  22. 22.(2013).
  23. 23.https://doi.org/10.1016/j.eurpolymj.2013.06.038DOI
  24. 24.T.-H. Zhao, W.-Q. Yuan, Y.-D. Li, Y.-X. Weng and J.-B. Zeng, Macromolecules, 2018, 51, 2027–2037.
  25. 25.Y. Chen, D. Yuan and C. Xu, ACS Appl. Mater. Interfaces, 2014, 6, 3811–3816.
  26. 26.7 J. Wu, Y.-W. Mai and A. F. Yee, J. Mater. Sci., 1994, 29, 4510– 4522.
  27. 27.S. L. Sun, X. Y. Xu, H. D. Yang and H. X. Zhang, Polymer, 2005, 46, 7632–7643.
  28. 28.D. Yuan, Z. Chen, C. Xu, K. Chen and Y. Chen, ACS Sustainable Chem. Eng., 2015, 3, 2856–2865.
  29. 29.M. L. Di Lorenzo, P. Rubino and M. Cocca, Eur. Polym. J., 2013, 49, 3309–3317.
  30. 30.O. Wachsen, K. Platkowski and K.-H. Reichert, Polym. Degrad. Stab., 1997, 57, 87–94
  31. 31.L. Yang, X. Chen and X. Jing, Polym. Degrad. Stab., 2008, 93, 1923–1929.
  32. 32.H. J. Lehermeier and J. R. Dorgan, Polym. Eng. Sci., 2001, 41, 2172–2184.
  33. 33.Y. Yuryev, A. K. Mohanty and M. Misra, RSC Adv., 2016, 6, 105094–105104.
  34. 34.G. M. Roudsari, A. K. Mohanty and M. Misra, ACS Omega, 2017, 2, 611–617.
  35. 35.Y. Chen, W. Wang, D. Yuan, C. Xu, L. Cao and X. Liang, ACS Sustainable Chem. Eng., 2018, 6, 6488–6496.
  36. 36.T.-H. Zhao, W.-Q. Yuan, Y.-D. Li, Y.-X. Weng and J.-B. Zeng, Macromolecules, 2018, 51, 2027–2037.
  37. 37.Y. Chen, D. Yuan and C. Xu, ACS Appl. Mater. Interfaces, 2014, 6, 3811–3816
  38. 38.D. Yuan, Z. Chen, C. Xu, K. Chen and Y. Chen, ACS Sustainable Chem. Eng., 2015, 3, 2856–2865.
  39. 39.O. Valerio, J. M. Pin, M. Misra and A. K. Mohanty, ACS Omega, 2016, 1, 1284–1295.
  40. 40.V. Ojijo and S. S. Ray, Polymer, 2015, 80, 1–17.
  41. 41.N. Zhang, C. Zeng, L. Wang and J. Ren, J. Polym. Environ., 2013, 21, 286–292.
  42. 42.M. L. Di Lorenzo, P. Rubino and M. Cocca, Eur. Polym. J., 2013, 49, 3309–3317.
  43. 43.M. W. Kim, S. M. Hong, D. Lee, K. Park, T. J. Kang and J. R. Youn, Adv. Compos. Mater., 2010, 19, 331–348.
  44. 44.J. Zhou, Z. Jiang, Z. Wang, J. Zhang, J. Li, Y. Li, J. Zhang, P. Chen and Q. Gu, RSC Adv., 2013, 3, 18464–18473.
  45. 45.L. G. Santos, L. C. Costa and L. A. Pessan, J. Appl. Polym. Sci., 2018, 135, 45951.
Download PDF
Cite This Article
Kuru, Z., Kaya, M. A. (2022). Improving the Properties of Biodegradable PLA via Blending with Polyesters for Industrial Applications. *The European Journal of Research and Development*, 2(4), 299-318. https://doi.org/10.56038/ejrnd.v2i4.201

Bibliographic Info

JournalThe European Journal of Research and Development
Volume2
Issue4
Pages299–318
PublishedDecember 31, 2022
eISSN2822-2296